Model No.: T6100
The T6100 series is Cold applied tape coating system for corrosion protection of Oil, Gas, Petrochemical, Waste Water underground or overhead pipelines and waterproofing.
The Bitumen tape shall be applied after the primer by hand or with a wrapping machine
The specification of the tape consists of three layers,
Backing:Special blend of stabilized polyolefines
Adhesive:Butyl rubber Bituminous Compound and Adhesion Promoting Resins
Interleaf:Antiadhesive Film Treated with Silicone
_ Heavy duty butyl bitumen compound adhesive
_ Excellent adhesion to pipe and self
_ Flexibility provides extra protection at vulnerable areas
_ Excellent conformability and consistent uniform thickness
_ Easily applied with no special equipment
_ Compatible with common pipe coatings
_ Excellent resistance to cathodic disbonding
_ Resistant to UV
_ Can be applied over a wide temperature range
_ Good conformability and consistent uniform thickness
_ Cold applied
IV Technical datas:
|PHYSICAL PROPERPTIES||UNIT||TEST METHOD||TYPICAL VALUES|
|Total thickness||mil||ASTM D 1000||40mils||50mils||60mils||65mils|
|Tensile Strength||lb/in||ASTM D 1000||30(5kg/cm)||35(6.3kg/cm)||39(7kg/cm)||42(7.5kg/cm)|
|Elongation||%||ASTM D 1000||400||400||450||500|
| Peel adhesion |
To primed pipe
|oz/in||ASTM D 1000||269(3kg/cm)||296(3.3kg/cm)||314 (3.5kg/cm)||340(3.8kg/cm)|
|To backing||oz/in||ASTM D 1000||90(1kg/cm)||90(1kg/cm)||117(1.3kg/cm)||135(1.5kg/cm)|
|Dielectric Strength||KV/mm||ASTM D 1000||42||42.6||43||43.8|
|Volume Resistivity||ohm·m||ASTM D 257||2.5 X 1012||2.5 X 1012||2.5 X 1012||2.5 X 1012|
|Water Vapor Transmission Rate||g/ m2 /24h||ASTM E 96||0.06||0.05||0.03||0.02|
|Water Absorptivity||%||ASTM D 570||0.1||0.1||0.1||0.1|
|Application Temperature||°F||-31-+160 (-35-+70ºC)|
|Max service temperature||°F||-40-+176 (-40-+80ºC)|
Contact us if you need more details on Pipe Wrap Tape. We are ready to answer your questions on packaging, logistics, certification or any other aspects about Butyl Tape、Bitumen Tape. If these products fail to match your need, please contact us and we would like to provide relevant information.
1.Add a halogen-containing flame retardant to polyethylene during processing. Bromine and chlorine are halogens used in fire-retardant compounds. Polyethylene is usually produced with fillers, unreactive compounds added to the polymer. Brominated compounds are the most widely used fire-retardant compounds. Add them instead...
As per our finding, the approximate market share for the given regions in 2014 is mentioned below. What is your take on this ? NOVISTA IS YOUR BEST CHOICE ON CPE
The global chlorinated polyethylene market is projected to grow from USD 395.4 Million in 2015 to USD 620.2 Million by 2021, at a CAGR of 8.0% between 2016 and 2021. Chlorinated polyethylene is a family of thermoplastics produced by the chlorination of high-density polyethylene. Based on grade, chlorinated polyethylene can...
Model NO.: RGT-BR Function: Anti-static, Heat Insulation, Sound-Absorbing, Waterproof, Seal Color: Grey or White or Yellow or Black Usage: Outdoor, Indoor Application: Waterproofing, Maintenance, Sealing Trademark: RJ JIAYE Transport Package: Packed by Cartons Specification: 5M/10M/15M/20M Origin: Shangdong Self adhesive...
Product Categories : Anticorrosive Tape